Multi Jet Fusion
Multi Jet Fusion, a technology introduced by the HP company, brings a real revolution to 3D printing of functional products. Discover a new technology that dramatically reduces the delivery time, offers high level of detail and excellent mechanical properties for functional prototypes and series production
Why is Multi Jet Fusion unique?
Thanks to the printer head definition of 1200 dpi and layer thickness of only 80 micrones, this technology moves powder sintering to the maximum level. It uses fine technical plastic granules and reaches almost 100% isotropic properties of products. A ground-breaking technology acts on the principle of fusion of basic powder materials with printing agents by blanket application of heat. This enables manufacture of products without supporting structures which further shortens the delivery time of functional prototypes and series production. This production system can print a volume of 40 l in a record time, only 10.5 hours.
Enjoy the possibility to freely design functional parts with an unrivalled manufacturing speed.
When is Multi Jet Fusion the most suitable?
- Customised packaging and casing for electronic devices
- Jigs, fixtures and robotic grippers with very complex shapes
- Lower- to medium-volume series of parts with complex shapes intended for end users
- Presentation and design models with high level of detail
- Prototypes with excellent mechanical properties
Get inspired by various applications of the Multi Jet Fusion technology and find the right use for you.
|Avarage lead-time||In avarage 3 to 5 working days depending on size and number of components and amount of finishing works|
|Print accuracy||0,2 mm and better|
|Layer thickness||80 micrometers|
|Minimum wall thickness||1 mm, 0,5 mm for flexible articulations|
|Print volume||380 x 284 x 380 mm|
Product dimensions are unlimited because they can be divided into multiple pieces, printed separately and then glued together
|Surface quality||Surface quality Parts after printing have smooth surface without visible signs of layering. They have grey color, can be sand-blasted, rumbled, died and impregnated with black color|
A versatile production printer with several materials with unique properties, suitable for dozens of different applications.
PA12 – a versatile material suitable for prototypes and functional parts. Wonderful mechanical properties, balanced ratio of strength, flexibility and elasticity. Download datasheet
|Density of parts||1,01 g/cm3||ASTM D792|
|Tensile strength, max load, XY, XZ, YX, YZ||48 MPa / 6960 psi||ASTM D638|
|Tensile strength, max load, ZX, ZY||48 MPa / 6960 psi||ASTM D638|
|Tensile modulus, XY, XZ, YX, YZ||1700 MPa / 245 ksi||ASTM D638|
|Tensile modulus, ZX, ZY||1800 MPa / 260 ksi||ASTM D638|
|Elongation at break, XY, XZ, YX, YZ||20%||ASTM D638|
|Elongation at break, ZX, ZY||15%||ASTM D638|
|Heat deflection temperature||175°C (@ 0.45 MPa, 66 psi)|
95°C (@ 1.82 MPa, 264 psi)